Plain carbon steel will still rust quite easily in most environments if not protected. Due to this, there are many ways steel has been modified to prevent corrosion. Two popular solutions are using a stainless steel or galvanized steel. While both steels resist rusting and corrosion, there are important differences between them that should be understood.
Stainless steel is able to resist corrosion because of the additional alloying elements in its chemical makeup. While plain carbon steel consists of mostly iron and carbon, stainless steel has substantial additions of chromium to help it resist corrosion. The chromium, and sometimes other alloying elements, are added to the stainless steel during the initial melting process, prior to it being formed into any particular shape.
Galvanized steel is a type of steel that has been coated in a layer of zinc that helps prevent the underlying steel from rusting. This layer is usually quite thin, often measured in thousandths of inches or microns. To create galvanized steel, the zinc layer is typically added well after melting, refining, and shaping of the steel plate or sheet. Sometimes it is even done after manufacturing processes have been performed on it such as bending or welding.
Stainless steel resists corrosion because of the added chromium (and sometimes other additional elements). Corrosion occurs on carbon steel when the iron from the steel is allowed to combine with oxygen in its surrounding environment. The chromium in stainless steel is able to prevent this as it combines with the oxygen and forms a passive layer of chromium oxide. This layer of chromium oxide prevents the formation of iron oxide, (also known as rust), in many situations, so long as the chromium content of the steel is great enough. Different grades of stainless steel designate and dictate the required amounts of chromium and other alloying elements, which helps to indicate the level of corrosion resistance.
Galvanized steel resists corrosion because of the zinc coating covering the carbon steel. The zinc layer serves two purposes:
Stainless steel usually has better corrosion-resistant properties than galvanized steel. If the stainless steel becomes scratched, it can still maintain corrosion resistance around the affected area. However, if the zinc layer of galvanized steel is damaged, it can leave the underlying carbon steel exposed and vulnerable. And because galvanized steel is often dipped in zinc in large sheets then cut to size, the edges where the cuts are made are left exposed making it possible for rust to occur.
Stainless steel is also generally considered to be more aesthetically pleasing than galvanized steel, as stainless typically has a shiny, silver-like color, versus the dull-grey pattern of galvanized steel. However, stainless steel is also often more expensive than galvanized steel.
Stainless steel is typically used in applications where the risk of corrosion is a major concern and not permissible. Areas of use for stainless steel include:
Galvanized steel is used for applications where corrosion is not desirable, but small amounts may be permissible and aesthetics are not much of a concern. Applications for galvanized steel include:
700mm UHP Graphite Electrode 600mm HP Graphite Electrode 450mm RP Graphite Electrode Hot Sale Galvanized Automotive Steel Galvanized Steel Automotive Steel Sheet Hand Sanitizer WingFlying Drone Thrust Test Drone Motor Test Stand Drone Test Equipment Hospital Beds And Home Care Beds Supplier Hospital Bed Wooden hospital beds hydroxypropyl methylcellulose wholesale Methyl Hydroxyethyl Cellulose Hydroxypropyl Methyl Cellulose